The aim of the present in vitro study was to evaluate specific mechanical and physicochemical properties of three calcium silicate-based sealers, BioRoot™ Flow (BRF), CeraSeal (CRS) and TotalFill® (TF). Samples were prepared to evaluate different physicochemical and mechanical properties of the tested sealers. These evaluations were accomplished by investigating the pH changes over time, porosity, roughness, flow properties, compressive strength and wettability. The results were statistically evaluated using one-way analysis of variance. All three sealers demonstrated an alkaline pH from 1 h of immersion in water to 168 h. A higher porosity and hydrophily were detected in BRF samples compared to CRS and TF. No significant difference was found between the tested materials in the flow properties. Lower compressive strength values were observed for BRF compared to TF and CRS. Differently shaped structures were detected on the three materials after 7 days of immersion in PBS. The three materials demonstrated a higher solubility than 3% after 24 h of immersion in water (CRS < BRF < TF). The novel premixed calcium silicate sealer (BRF) had comparable physicochemical properties to the existing sealers. The lower compressive strength values could facilitate the removal of these materials during retreatment procedures. Further studies should investigate the biological effects of the novel sealer.