Oxidation state variation under beta-irradiation in an iron-bearing soda lime glass system - École polytechnique Access content directly
Conference Papers Year : 2009

Oxidation state variation under beta-irradiation in an iron-bearing soda lime glass system

Abstract

The effect of ionizing radiation on glasses in the system SiO2-CaO-Na2O-Fe2O3 is investigated as a function of iron concentration or / and irradiation dose by a pre-edge analysis at the iron K-edge. While reduction phenomenon is clearly observed for large irradiation doses (5 C), the effect of irradiation for intermediate doses is more challenging to interpret. Comparison between X-ray absorption measurements, colorimetry results and Electron Paramagnetic Resonance measurements suggest that iron environment may be modified without the ions being reduced.

Keywords

Fichier principal
Vignette du fichier
rossanoetal09.pdf (760.88 Ko) Télécharger le fichier
Origin : Publisher files allowed on an open archive
Loading...

Dates and versions

hal-00512619 , version 1 (31-08-2010)

Identifiers

Cite

Stéphanie Rossano, Liliane Jean-Soro, Bruno Boizot, Francois Farges, Eric D. van Hullebusch, et al.. Oxidation state variation under beta-irradiation in an iron-bearing soda lime glass system. 14th International Conference on X-Ray Absorption Fine Structure (XAFS14), Jul 2009, Camerino, Italy. pp.012194, ⟨10.1088/1742-6596/190/1/012194⟩. ⟨hal-00512619⟩
471 View
448 Download

Altmetric

Share

Gmail Facebook X LinkedIn More