Divalent Europium in beta irradiated aluminoborosilicate glass

Abstract

The reduction processes of Eu3+ ions in aluminoborosilicate glasses were studied using both high-temperature melting in air and b-irradiation by time-resolved luminescence and electron paramagnetic resonance spectroscopies. The Eu2+ ions produced during the synthesis are characterized by the UV excited broadband luminescence in the blue region due to the 4f 65d1–4f7 transition. This band revealed the presence more than one Eu2+ site participating in the emission with different crystalline fields and with different covalency of surrounding ligands. In irradiated glasses, the observed redshift of the Eu2+ emission band is related to the different relative proportion between Eu2+ sites.
Fichier principal
Vignette du fichier
malchukovaetal_2010_jacs.pdf (194.22 Ko) Télécharger le fichier
Origin : Files produced by the author(s)
Loading...

Dates and versions

hal-00546740 , version 1 (14-12-2010)

Identifiers

Cite

Evguenia Malchukova, Bruno Boizot. Divalent Europium in beta irradiated aluminoborosilicate glass. Journal of the American Ceramic Society, 2010, 93 (12), pp.4005-4007. ⟨10.1111/j.1551-2916.2010.04209.x⟩. ⟨hal-00546740⟩
102 View
184 Download

Altmetric

Share

Gmail Facebook X LinkedIn More